MATERIALS ENGINEERING
SEMINAR

"Design and Processing of NiCo-based Superalloys for the Study of Solute Segregation at Planar Defects During High Temperature Deformation"
By
Sae Matsunaga
Purdue MSE Ph.D. Final Exam

Advisors: Professor Michael Titus

ABSTRACT

Ni-based superalloys have been widely used for high temperature applications such as turbine blades for jet propulsion and power plants due to their excellent creep, fatigue, and corrosion resistance. But as the demand for higher temperature capability and strength increases, there remains a need to better understand high temperature deformation mechanisms and improve and strengthen superalloys at these elevated temperatures. Recently, a correlation has been observed between solute segregation at planar defects (stacking faults, antiphase boundaries, etc) and enhanced high temperature creep properties - known colloquially as phase transformation strengthening. Experimentally, regardless of alloy composition, strong Co segregation at planar defects along with Cr has been observed. In addition, it has been suggested by density functional theory work that Co would promote Cr concentration at stacking faults by forming strong Cr-Co bonds. Based on these findings, it was hypothesized the presence of Co provides a significant thermodynamic driving force for segregation to planar defects.
In order to further investigate the correlation between solute segregation and deformation mechanisms the fabrication of a planar front single crystal Ni-based superalloy and its microstructure, alloy composition, and microhardness properties of the as-zone melted and solution heat treated states were investigated and compared to the directionally-solidified state to study the effect of microsegregation on these alloy characteristics. Next, new Co-containing, Cr-free alloys are designed to optimize gamma-gamma' volume fraction, size, and morphology to mimick microstructures observed in single crystal superalloys. The general alloy design strategy and approach are outlined, and the composition, microstructure, phase transformation temperatures, and mechanical properties of new Cr-free and Co-containing alloys are reported. A new set of Cr-free alloys have thus been designed, with modifications of Nb, Ta, and Ti additions ranging from 3 to 7 at.% to investigate the role of these elements on the phase transformation strengthening mechanism at elevated temperatures.



Date: Monday, November 22, 2021

Time: 1:30 P.M.
Place: HAMP 1266
or Join from the meeting link
https://purdue.webex.com/purdue/j.php?MTID=mf23fce9475ea4d01fefa71ab1edf8013


PURDUE MSE
[cid:image002.png at 01D7D4C0.5C6CEA10]





-------------- next part --------------
An HTML attachment was scrubbed...
URL: </ECN/mailman/archives/msepostdoc-list/attachments/20211108/aef52ceb/attachment-0001.htm>
-------------- next part --------------
A non-text attachment was scrubbed...
Name: image001.wmz
Type: application/x-ms-wmz
Size: 5833 bytes
Desc: image001.wmz
URL: </ECN/mailman/archives/msepostdoc-list/attachments/20211108/aef52ceb/attachment-0001.wmz>
-------------- next part --------------
A non-text attachment was scrubbed...
Name: image002.png
Type: image/png
Size: 5308 bytes
Desc: image002.png
URL: </ECN/mailman/archives/msepostdoc-list/attachments/20211108/aef52ceb/attachment-0001.png>
-------------- next part --------------
A non-text attachment was scrubbed...
Name: oledata.mso
Type: application/octet-stream
Size: 7652 bytes
Desc: oledata.mso
URL: </ECN/mailman/archives/msepostdoc-list/attachments/20211108/aef52ceb/attachment-0001.obj>
-------------- next part --------------
A non-text attachment was scrubbed...
Name: Final Exam Seminar Announcement Sae Matsunaga.docx
Type: application/vnd.openxmlformats-officedocument.wordprocessingml.document
Size: 32848 bytes
Desc: Final Exam Seminar Announcement Sae Matsunaga.docx
URL: </ECN/mailman/archives/msepostdoc-list/attachments/20211108/aef52ceb/attachment-0001.docx>